Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Saturation,23°C | ISO62 | 0.80 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | 23°C | ISO527-2 | 25 | % |
Tensile Modulus | 23°C | ISO527-2 | 2810 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2340 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 62.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 10 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | 1.5mm | UL746 | 105 | °C |
RTIElec | 3.0mm | UL746 | 105 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 90.0 | °C |
Evolution Calendar intelligent importer | 3.0mm | UL746 | 90.0 | °C |
RTIStr | 1.5mm | UL746 | 90.0 | °C |
RTIStr | 3.0mm | UL746 | 105 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 151 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 96.0 | °C |
Melting temperature (DSC) | | ISO3146 | 167 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Dielectric Constant | 100Hz | IEC60250 | 3.80 | |
Dielectric Constant | 1MHz | IEC60250 | 3.80 | |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 5E-03 | |
Dielectric Strength | | IEC60243-1 | 40 | KV/mm |
Comparative Tracking Index | | IEC60112 | 600 | V |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.