Technical Data Sheet
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield,23℃ | MPa | ASTM D638 | 55.0 |
Flexural Modulus | 23°C | MPa | ASTM D790 | 2200 |
Flexural Strength | 23°C | MPa | ASTM D790 | 80.0 |
IZOD Notch Impact Strength | 23°C | J/m | ASTM D256 | 80.0 |
Tensile Elongation?(Break) | Yield,23℃ | % | ASTM D638 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | flow | cm/cm/°C | ASTM D696 | 0.00013 |
Melting temperature | | | °C | 166 |
Thermal distortion temperature | 0.45MPa,Unannealed | °C | ASTM D648 | 158 |
Thermal distortion temperature | 1.8MPa,Unannealed | °C | ASTM D648 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1E+6 Hz | | ASTM D150 | 0.0060 |
Surface Resistivity | | ohms | ASTM D257 | |
Dielectric Constant | | | ASTM D150 | 3.70 |
Volume Resistivity | | ohm·cm | ASTM D257 | |
Dielectric Strength | | kV/mm | ASTM D149 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | flow | % | ASTM D955 | 2.0 |
Moisture Absorption | Equilibrium,23℃,60%rh | % | ASTM D570 | 0.21 |
Rockwell Hardness | M-Scale | | ASTM D785 | |
Melt Mass-Flow Rate | 190℃/2.16kg | g/10 min | ASTM D1238 | |
Density | | g/cm³ | ASTM D792 | 1.40 |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.