Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | 内部方法 | 1.8到2.2 | % |
| Moisture Absorption | 23°C,24hr,50%RH | ASTMD570 | 0.20 | % |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 1.7 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber Abrasion Resistance | | ASTMD1044 | 13.0 | mg |
| Tensile Stress | Yield | ISO527-2 | 75.0 | Mpa |
| Tensile Stress | -- | ASTMD638 | 79.0 | Mpa |
| Tensile Modulus | | ISO527-2 | 3150 | Mpa |
| Tensile Elongation | Break | ASTMD638,ISO527-2 | 40 | % |
| Flexural Modulus | -- | ASTMD790 | 3040 | Mpa |
| Flexural Modulus | -- | ISO178 | 2900 | Mpa |
| Flexural Strength | | ASTMD790 | 108 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 172 | °C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 167 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 136 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 103 | °C |
| Specific Heat | | | 1470 | J/kg/°C |
| Thermal Conductivity | | | 0.23 | W/m/K |
| Linear thermal expansion coefficient | MD | ASTMD696,ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | ASTMD149 | 18 | KV/mm |
| Dissipation Factor? | 23°C,1MHz | ASTMD150 | 7E-03 | |
| Surface Resistivity | | ASTMD257 | 1.0E+16到1.0E+17 | ohms |
| Dielectric Constant | 23°C,1MHz | ASTMD150 | 3.80 | |
| Arc Resistance | | ASTMD495 | 250 | sec |
| Volume Resistivity | 23°C | ASTMD257 | 1.0E+15到1.0E+16 | ohms·cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ASTMD785 | 94 | |
| Rockwell Hardness | R-Scale | ASTMD785 | 120 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.