Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.90 | % |
| Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.35 | % |
| Modeling Shrinkage | TD | ISO294-4 | 1.4 | % |
| Modeling Shrinkage | MD | ISO294-4 | 1.3 | % |
| Melt Mass-Flow Rate | | ISO1133 | 2.0 | g/10min |
| MediumDensity | | | 1.14 | g/cm³ |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 1.70 | cm3/10min |
| Density / Specific Gravity | | ISO1183 | 1.34 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2 | >50 | % |
| Flexural Stress | 3.5%Strain | ISO178 | 34.0 | Mpa |
| Tensile Creep Modulus | 1hr | ISO899-1 | 1100 | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 550 | Mpa |
| Tensile Stress | Yield | ISO527-2 | 41.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 30 | % |
| Tensile Modulus | | ISO527-2 | 1400 | Mpa |
| Flexural Modulus | | ISO178 | 1100 | Mpa |
| CoefficientFriction | vs.Itself-Dynamic,1hr | ASTMD1894 | 0.32 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Annealing Temperature | | | 160 | °C |
| Annealing Time-Optional | | | 30.0 | min/mm |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 100 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 60.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| Melting Temperature | | ISO11357-3 | 178 | °C |
| Glass Transition Temperature | | ISO11357-2 | -35.0 | °C |
| Effective Thermal Diffusivity | | | 6E-08 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.40 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.80 | |
| Comparative Tracking Index | | IEC60112 | 600 | V |
| Surface Resistivity | | IEC60093 | 1E+14 | ohms |
| Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 18 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 90 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 20 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 90 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Sale | ISO2039-2 | 58 | |
| Rockwell Hardness | R-Sale | ISO2039-2 | 105 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | 41 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 2.90 | µgC/g |
| Emission | | VDA275 | <8.00 | mg/kg |
| SpecificWear-Againstitself | | ASTMD1894 | 60.0 | 10^-6mm³/N·m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.