POM DURACON® MS-02 JAPAN POLYPLASTIC
133
- Unit Price:
- $6452 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low friction coefficient Lubricity
- Application Areas:Electronic and electrical Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | % | ASTM D638 | |
| Break | % | ISO 527-2 | ||
| Flexural Modulus | MPa | ASTM D790 | 2510 | |
| MPa | ISO 178 | 2500 | ||
| Flexural Strength | MPa | ASTM D790 | 96 | |
| MPa | ISO 178 | 84 | ||
| Notched Impact Strength | J/m | ASTM D256 | 55 | |
| Charpy Notched Impact Strength | kJ/m² | ISO 179/1eA | 4.8 | |
| Reverse Notched Impact Strength | J/m | ASTM D256 | ||
| Tensile Stress(Yield) | MPa | ISO 527-2 | 64 | |
| MPa | ASTM D638 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | UL 94 | HB | ||
| Coefficient of Linear Thermal Expansion (Flow) | 23℃ | cm/cm/℃ | ASTM D696 | 0.00010 |
| Coefficient of Linear Thermal Expansion (Across Flow) | 23℃ | cm/cm/℃ | ASTM D696 | 0.00010 |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ℃ | ASTM D648 | |
| 1.8MPa,Unannealed | ℃ | ISO 75-2A | 81 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.