POM DURACON® CH-15 JAPAN POLYPLASTIC

Unit Price:
$7269 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
14MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	190°C/2.16 kg	ISO 1133	3.0	g/10 min
Melt Volume flow Rate	190°C/2.16 kg	ISO 1133	2.40	cm3/10min
Density		ISO 1183	1.45	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ISO 527-2	11700	Mpa
Flexural Modulus		ISO 178	10000	Mpa
Tensile Stress		ISO 527-2	130	Mpa
Tensile Strain	Break	ISO 527-2	1.5	%
Flexural Stress		ISO 178	185	Mpa
Coefficient of Friction	Dynamic 2	JIS K7218	0.37
Coefficient of Friction	Coefficient of Friction	与钢 - 动态 3	JIS K7218	0.27
Specific Wear Rate	0.49 MPa, 0.30 m/sec 4	JIS K7218	10	10^-8 mm³/N·m
	Specific Wear Rate	0.060 MPa, 0.15 m/sec 5	JIS K7218	200	10^-8 mm³/N·m
		Specific Wear Rate	0.49 MPa, 0.30 m/sec 6	JIS K7218	500	10^-8 mm³/N·m
		Specific Wear Rate	Specific Wear Rate	0.060 MPa, 0.15 m/sec 7	JIS K7218	10000	10^-8 mm³/N·m

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : 23 to 55°C	内部方法	1.0E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	内部方法	9.0E-5	cm/cm/°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	163	°C

Electrical performance	Test Method	Test Result	Unit
Surface Resistivity	IEC 60093	3.0E+2	ohms
Volume Resistivity	IEC 60093	1.0E+3	ohms·cm
Color Number		CD3501

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Screw Speed	100 到 150	rpm
Injection Pressure	50.0 到 100	Mpa
Injection Velocity	0 到 3	m/min
Drying Temperature	80 到 90	°C
Processing (Melt) Temp	190 到 210	°C
Mold Temperature	60 到 80	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.5	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.