POM Delrin® 570 DUPONT USA
109
- Unit Price:
- $10466 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 57MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Filler: Glass fiber reinf 20% filler by weight UV resistance wear resistant
- Application Areas:Electrical tools household electrical appl
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.2 | % |
| MD | ISO294-4 | 1.8 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.80 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.10 | % | |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 7.00 | cm3/10min |
| Density / Specific Gravity | ISO1183 | 1.56 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO527-2 | 53.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 12 | % |
| Tensile Modulus | ISO527-2 | 4900 | Mpa | |
| Flexural Modulus | ISO178 | 4600 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 165 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
| Melting Temperature | ISO11357-3 | 178 | °C | |
| Annealing Temperature | 160 | °C | ||
| Annealing Time-Optional | 30.0 | min/mm | ||
| Vicat Softening Temperature | ISO306/B50 | 160 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.90 | ||
| Comparative Tracking Index | IEC60112 | 600 | V | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 50 | kJ/m² |
| 23°C | ISO179/1eU | 54 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.0 | kJ/m² |
| 23°C | ISO179/1eA | 3.5 | kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 6.0 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| FMVSS Flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 5E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | 53 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 4.80 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.