Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.42 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 22 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM D570 | 0.2 | % |
Moisture Absorption | 23°C,24hr,50%RH | ASTMD570 | 0.20 | % |
Modeling Shrinkage | MD | 内部方法 | 1.8到2.2 | % |
Modeling Shrinkage | -,Flow | | 1.8-2.2 | % |
Modeling Shrinkage | -,Across Flow | | 1.8-2.2 | % |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 22 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | | ASTMD1044 | 13.0 | mg |
Taber Abrasion Resistance | | ASTM D1044 | 13 | |
Tensile Elongation | | ASTM D638 | 45 | % |
IZOD Notch Impact Strength | | ASTM D256 | 69 | J/m |
Tensile Stress | Yield | ISO527-2 | 72.0 | Mpa |
Tensile Stress | -- | ASTMD638 | 72.0 | Mpa |
Tensile Modulus | | ISO527-2 | 3300 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 69 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638 | 69 | Mpa |
Tensile Elongation | | ASTM D638/ISO 527 | 45 | % |
Tensile Elongation | Break | ASTMD638,ISO527-2 | 30 | % |
Rockwell Hardness | | ASTM D785 | 120 | R |
Rockwell Hardness | | ASTM D785 | 94 | |
Flexural Modulus | | ASTM D790/ISO 178 | 3040 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790 | 3040 | Mpa |
Flexural Modulus | -- | ASTMD790 | 3040 | Mpa |
Flexural Modulus | -- | ISO178 | 3100 | Mpa |
Flexural Strength | | ASTMD790 | 107 | Mpa |
Flexural Strength | | ASTM D790 | 103 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 103 | kg/cm²(MPa)[Lb/in²] |
Izod notch impact strength | | ASTM D256/ISO 179 | 69 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | ASTMD696,ISO11359-2 | 1E-04 | cm/cm/°C |
Flame retardancy | | UL94 | HB | |
Burning Rate | | UL94 | HB | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 136(1.8Mpa) | ℃(℉) |
Deflection Temperature Under Load? | -,1.82MPa | ASTM D648 | 136 | °C |
Deflection Temperature Under Load? | -,0.45MPa | ASTM D648 | 172 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 172 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 165 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 136 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 105 | °C |
Coefficient of Linear Thermal Expansion | | | 10 | |
Melt index | | ASTM D1238 | 22 | g/10min |
Specific Heat | | | 1470 | J/kg/°C |
Thermal Conductivity | | | 0.23 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | ASTMD149 | 18 | KV/mm |
Dissipation Factor? | 23°C,1MHz | ASTMD150 | 7E-03 | |
Surface Resistivity | | ASTMD257 | 1.0E+16到1.0E+17 | ohms |
Dielectric Constant | 23°C,1MHz | ASTMD150 | 3.80 | |
Arc Resistance | | ASTMD495 | 250 | sec |
Volume Resistivity | 23°C | ASTMD257 | 1.0E+15到1.0E+16 | ohms·cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 94 | |
Rockwell Hardness | R-Scale | ASTMD785 | 120 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.