Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.00mm | ASTMD955 | 2.0 | % |
Moisture Absorption | Equilibrium,23°C,60%RH | ASTMD570 | 0.22 | % |
Melt Mass-Flow Rate | | ASTMD1238 | 9.0 | g/10min |
Density / Specific Gravity | | ASTMD792 | 1.41 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield,23°C | ASTMD638 | 61.0 | Mpa |
Shearing Strength | 2.00mm | ASTMD732 | 55.0 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 60 | % |
Flexural Modulus | 23°C | ASTMD790 | 2600 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 90.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 158 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 110 | °C |
Deflection Temperature Under Load? | Melting Temperature | ASTMD648 | 165 | °C |
Linear thermal expansion coefficient | MD:20to80°C | ASTMD696 | 1.3E-04 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | ASTMD149 | 19 | KV/mm |
Dissipation Factor? | 1MHz | ASTMD150 | 7E-03 | |
Surface Resistivity | | ASTMD257 | 1E+16 | ohms |
Dielectric Constant | 1MHz | ASTMD150 | 3.70 | |
Volume Resistivity | | ASTMD257 | 1E+14 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 3.20mm | ASTMD256 | 64 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 80 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.800mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.