Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 0.917 | |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 35 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | | ASTMD1238 | 35 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength(Break) | | ASTM D-638 | 100 | kg/cm2 |
Flexural Modulus | | ASTMD747 | 180 | Mpa |
Tensile Strength | Break | ASTMD638 | 9.80 | Mpa |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 600 | % |
Tensile Strength | | ASTM D638/ISO 527 | 9.8 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D-638 | 600 | % |
Tensile Elongation | Break | ASTMD638 | 600 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | | 105 | ℃(℉) |
Melting temperature | | 内部方法 | 105 | °C |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | | ASTM D-1238 | 35 | g/10min |
Density | | ASTM D-792 | 0.917 | g/cm³ |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strength | | ASTM D-747 | 1800 | kg/cm2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.