PMMA Altuglas® V825T-101 ARKEMA ITALY

173

Unit Price:
$7990 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:transparent wear resistant High temperature resistan
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.30	%
Melt Mass-Flow Rate	230°C/3.8 kg	ISO 1133	2.8	g/10 min
Modeling Shrinkage - Flow		ASTM D955	0.20 到 0.60	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	23°C	ISO 178	103	Mpa
Tensile Stress	Yield, 23°C	ISO 527-2	70.0	Mpa
Tensile Strain	Break, 23°C	ISO 527-2	6.0	%
Flexural Modulus	23°C	ISO 178	3300	Mpa
Compressive Stress	23°C	ISO 604	117	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	103	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	100	°C
Vicat Softening Temperature		ISO 306/B	108	°C
Coefficient of Linear Thermal Expansion (Flow)	-30 to 23°C	ASTM D696	6.5E-5	cm/cm/°C
Specific Heat			2090	J/kg/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1 MHz	ASTM D150	0.040
Dielectric Strength		ASTM D149	20	KV/mm
Surface Resistivity		ASTM D257	> 1.0E+14	ohms
Dielectric Constant	60 Hz	ASTM D150	3.70
Volume Resistivity		ASTM D257	> 1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	85 到 90	°C
Processing (Melt) Temp	230 到 250	°C
Mold Temperature	80 到 90	°C
Drying Time	2.0 到 4.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO 179/2U	11	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	97

optical performance	Test Method	Test Result	Unit
Transmittance	ASTM D1003	92.0	%
Haze	ASTM D1003	0.50	%
Index of Refraction	ISO 489	1.490

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating		UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.