Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | N | ISO 489 | 1.49 | |
| Haze | 3mm | ISO 14782 | 0.3 | % |
| Light Transmittance | 3mm | ISO 13468-1 | 93 | % |
| Density / Specific Gravity | | ISO 1183 | 1.19 | g/cm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | 1A/5 | ISO 527-2 | 78 | Mpa |
| Tensile Elongation | 1A/1 | ISO 527-2 | 3.3 | GPa |
| Flexural Strength | | ISO 178 | 127 | Mpa |
| Flexural Modulus | | ISO 178 | 3.3 | GPa |
| Notched Izod Impact Strength | 1eA V槽口 | JIS K-7111 | 1.3 | KJ/m |
| Notched Izod Impact Strength | 1eU 无槽口 | JIS K-7111 | 21 | KJ/m |
| Tensile Elongation | 1A/5 | ISO 527-2 | 6 | % |
| Rockwell Hardness | | ISO 2039 | 101 | M Scale |
| Izod Impact Strength | 1A | JIS K-7110 | 1.7 | KJ/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | 50n | ISO 306 | 108 | °C |
| Deflection Temperature Under Load | 1.80MPa | ISO 75-2 | 101 | °C |
| Coefficient of Linear Thermal Expansion | | JIS K-7197 | 6×10 | 1/℃ |
| Thermal Conductivity | | JIS A-1412 | 0.2 | W/(m·℃) |
| Specific Heat | | JIS K-7123 | 1.5 | J/(g·℃) |
| Spiral Flow | 厚薄2mm,230℃ | 三菱丽阳法 | 130 | mm |
| Spiral Flow | 厚薄2mm,250℃ | 三菱丽阳法 | 220 | mm |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | JIS K-6911 | >10 | Ωm |
| Dissipation Factor | 60Hz | JIS K-6911 | 0.05 | |
| Insulation Resistance | 4kV/sec | JIS K-6911 | 20 | MV/m |
| Surface Resistivity | | JIS K-6911 | >10 | Ω |
| Dielectric Constant | 60Hz | JIS K-6911 | 3.7 | |
| Arc Resistance | | JIS K-6911 | 没有痕迹 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 24hr | ISO 62 | 0.3 | % |
| Melt index | 230℃,37.3N | ISO 1133 | 2.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.