PA66 Vydyne® R515NT ASCEND USA
368
- Unit Price:
- $4099 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Gear Power/Other Tools Parts under the hood of a Shell
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:23°C,2.00mm | ISO294-4 | 1.0 | % |
| MD:23°C,2.00mm | ISO294-4 | 0.50 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 1.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.2 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break,23°C | ISO527-2 | 120 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 3.0 | % |
| Flexural Stress | 23°C | ISO178 | 170 | Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 6600 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 5900 | Mpa |
| Poisson Ratio | ISO527-2 | 0.40 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 258 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 241 | °C | |
| RTIElec | 0.75mm | UL746 | 120 | °C |
| 1.5mm | UL746 | 120 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 85.0 | °C |
| 1.5mm | UL746 | 85.0 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| RTIStr | 0.75mm | UL746 | 115 | °C |
| 1.5mm | UL746 | 120 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| Linear thermal expansion coefficient | MD：23to55°C,2.00mm | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD：23to55°C,2.00mm | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature | ISO11357-3 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc Resistance | 3.00mm | ASTMD495 | PLC5 | |
| Dielectric Strength | 1.00mm | IEC60243 | 24 | KV/mm |
| Comparative Tracking Index | 3.00mm | IEC60112 | 600 | V |
| Volume Resistivity | 0.750mm | IEC60093 | 1E+13 | ohms·cm |
| High Amp Arc Ignition | 0.75mm | UL746 | PLC0 | |
| 1.5mm | UL746 | PLC0 | ||
| 3.0mm | UL746 | PLC0 | ||
| Hot-wire Ignition | 0.75mm | UL746 | PLC4 | |
| 1.5mm | UL746 | PLC4 | ||
| 3.0mm | UL746 | PLC4 | ||
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 32 | kJ/m² |
| 23°C | ISO179 | 39 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.