Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.3 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.20 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 5.2to5.8 | % |
| HumidityAbsorption-62%RH | 70°C | ISO1110 | 1.9to2.1 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO178 | 8500 | Mpa |
| Flexural Stress | | ISO178 | 280 | Mpa |
| Tensile Stress | Break | ISO527-2/5 | 190 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 3.5 | % |
| Tensile Modulus | | ISO527-2/1 | 9500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 255 | °C |
| Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 210 | °C |
| Linear thermal expansion coefficient | MD：23to80°C | ISO11359-2 | 1.9E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：23to80°C | ISO11359-2 | 9.5E-05 | cm/cm/°C |
| Melting Temperature | | DINEN11357-1 | 262 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 85 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.6mm | UL94 | HB | |
| Burning Rate | 1.00mm | FMVSS302 | <100 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| ReinforcementContent | | ISO1172 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.