PA66 66G25V0P BK DOMO CHEM GERMANY

Unit Price:
$46216 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ISO 1183	1.39	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus		ISO 178	7000	Mpa
Flexural Stress		ISO 178	170	Mpa
Tensile Modulus		ISO 527-2/1	8000	Mpa
Tensile Stress	Break	ISO 527-2/5	110	Mpa
Tensile Strain	Break	ISO 527-2/5	2.5	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Melting temperature		ISO 11357-3	262	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	240	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	220	°C
Vicat Softening Temperature		ISO 306/B50	235	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC 60093	1.0E+13	ohms
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm
Comparative Tracking Index	Solution A	IEC 60112	375	V

Injection	Test Result	Unit
Drying Temperature	75 到 85	°C
Processing (Melt) Temp	270 到 290	°C
Mold Temperature	80 到 100	°C
Drying Time	2.0 到 4.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	23°C	ISO 180/1U	30	kJ/m²
Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	35	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.5	kJ/m²
Notched Izod Impact Strength	23°C	ISO 180/1A	5.5	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0 to 3.0 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0 to 3.0 mm	IEC 60695-2-13	775	°C
Burning Rate		FMVSS 302	< 100	mm/min
Flame Rating	0.8 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.