PA66 Vydyne® R550H BK ASCEND USA

Unit Price:
$4235 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:23°C,2.00mm	ISO294-4	0.90	%
Modeling Shrinkage	Modeling Shrinkage	MD:23°C,2.00mm	ISO294-4	0.40	%
Moisture Absorption	23°C,24hr	ISO62	0.50	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	1.2	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break,23°C	ISO527-2	240	Mpa
Tensile Strain	Break,23°C	ISO527-2	2.5	%
Tensile Modulus	23°C	ISO527-2	16800	Mpa
Flexural Modulus	23°C	ISO178	16000	Mpa
Flexural Strength	23°C	ISO178	350	Mpa
Poisson Ratio		ISO527-2	0.40

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	260	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	255	°C
RTIElec	3.0mm	UL746	140	°C
	RTIElec	0.75mm	UL746	140	°C
	RTIElec	RTIElec	1.5mm	UL746	140	°C
Evolution Calendar intelligent importer	0.75mm	UL746	130	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	130	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	130	°C
RTIStr	0.75mm	UL746	140	°C
	RTIStr	1.5mm	UL746	140	°C
	RTIStr	RTIStr	3.0mm	UL746	140	°C
Linear thermal expansion coefficient	MD：23to55°C,2.00mm	ISO11359-2	1.2E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C,2.00mm	ISO11359-2	1E-04	cm/cm/°C
Melting temperature		ISO11357-3	260	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	1.00mm	IEC60243	20	KV/mm
Comparative Tracking Index	3.00mm	IEC60112	400to599	V
Volume Resistivity	0.750mm	IEC60093	1E+12	ohms·cm
High Amp Arc Ignition	0.75mm	UL746	PLC0
	High Amp Arc Ignition	1.5mm	UL746	PLC0
	High Amp Arc Ignition	High Amp Arc Ignition	3.0mm	UL746	PLC0
Hot-wire Ignition	0.75mm	UL746	PLC4
	Hot-wire Ignition	1.5mm	UL746	PLC3
	Hot-wire Ignition	Hot-wire Ignition	3.0mm	UL746	PLC4
Arc Resistance	3.00mm	ASTMD495	PLC5
High Voltage Arc Tracking Rate	HVTR	UL746	PLC1

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	91	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	95	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Ignition Temperature	0.75mm	IEC60695-2-13	700	°C
	Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	700	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	750	°C
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	HB
Glow Wire Flammability Index	0.75mm	IEC60695-2-12	675	°C
	Glow Wire Flammability Index	1.5mm	IEC60695-2-12	675	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C

Supplementary information	Test Condition	Test Method	Test Result	Unit
AutomotiveMaterials-	thicknessd=1mm	FMVSS302	+

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.