PA66 LATAMID 66 H2 G/25 V0 CT1 LATI ITALY
133
- Unit Price:
- $7190 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 25% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:2.00mm | ISO294-4 | 0.70到1.0 | % |
| MD:2.00mm | ISO294-4 | 0.35到0.60 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.25 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield,120°C | ISO527-2/5 | 60.0 | Mpa |
| Yield,150°C | ISO527-2/5 | 50.0 | Mpa | |
| Break,23°C | ISO527-2/5 | 135 | Mpa | |
| Break,60°C | ISO527-2/5 | 95.0 | Mpa | |
| Break,90°C | ISO527-2/5 | 75.0 | Mpa | |
| Break,120°C | ISO527-2/5 | 60.0 | Mpa | |
| Break,150°C | ISO527-2/5 | 50.0 | Mpa | |
| Tensile Strain | Yield,120°C | ISO527-2/5 | 3.5 | % |
| Yield,150°C | ISO527-2/5 | 3.7 | % | |
| Break,23°C | ISO527-2/5 | 2.1 | % | |
| Break,60°C | ISO527-2/5 | 2.4 | % | |
| Break,90°C | ISO527-2/5 | 3.8 | % | |
| Break,120°C | ISO527-2/5 | 3.9 | % | |
| Break,150°C | ISO527-2/5 | 4.2 | % | |
| Tensile Modulus | 23°C | ISO527-2/1 | 9200 | Mpa |
| 60°C | ISO527-2/1 | 7200 | Mpa | |
| 150°C | ISO527-2/1 | 2200 | Mpa | |
| 120°C | ISO527-2/1 | 3200 | Mpa | |
| 90°C | ISO527-2/1 | 4800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 255 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 240 | °C | |
| 连续使用温度4 | 115 | °C | ||
| Vicat Softening Temperature | ISO306/B50 | 245 | °C | |
| Linear thermal expansion coefficient | MD：30to100°C | ISO11359-2 | 8E-06 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | SolutionA | IEC60112 | 400 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 35 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | V-0 | ||
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
| 2.0mm | IEC60695-2-12 | 960 | °C | |
| Oxygen Index | ASTMD2863 | 35 | % | |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 900 | °C |
| 2.0mm | IEC60695-2-13 | 900 | °C |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| DimensionalStability | 21.0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.