PA66 Vydyne® R535H BK ASCEND USA

Unit Price:
$3742 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow : 2.00 mm	ISO 294-4	0.90	%
Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm	ISO 294-4	0.40	%
Moisture Absorption	24 hr, 23°C	ISO 62	0.80	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	1.6	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break, 23°C	ISO 527-2	210	Mpa
Tensile Strain	Break, 23°C	ISO 527-2	3.0	%
Tensile Modulus	23°C	ISO 527-2	11600	Mpa
Flexural Modulus	23°C	ISO 178	10500	Mpa
Flexural Stress	23°C	ISO 178	300	Mpa
Poisson Ratio		ISO 527	0.40

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	2.0E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	1.1E-4	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	260	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	250	°C
RTI	0.75 mm	UL 746	140	°C
	RTI	1.5 mm	UL 746	140	°C
	RTI	RTI	3.0 mm	UL 746	140	°C
RTI Imp	0.75 mm	UL 746	125	°C
	RTI Imp	1.5 mm	UL 746	125	°C
	RTI Imp	RTI Imp	3.0 mm	UL 746	125	°C
RTI Elec	0.75 mm	UL 746	140	°C
	RTI Elec	1.5 mm	UL 746	140	°C
	RTI Elec	RTI Elec	3.0 mm	UL 746	140	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
High Amp Arc Ignition	0.75 mm	UL 746	PLC 0
	High Amp Arc Ignition	1.5 mm	UL 746	PLC 0
	High Amp Arc Ignition	High Amp Arc Ignition	3.0 mm	UL 746	PLC 0
Hot-wire Ignition	0.75 mm	UL 746	PLC 4
	Hot-wire Ignition	1.5 mm	UL 746	PLC 3
	Hot-wire Ignition	Hot-wire Ignition	3.0 mm	UL 746	PLC 4
High Voltage Arc Tracking Rate		UL 746	PLC 1
Arc Resistance	3.00 mm	ASTM D495	PLC 6
Volume Resistivity	0.750 mm	IEC 60093	1.0E+13	ohms·cm
Dielectric Strength	1.00 mm	IEC 60243	20	KV/mm
Comparative Tracking Index	3.00 mm	IEC 60112	250 到 399	V

Injection	Test Result	Unit
Drying Temperature	80	°C
Processing (Melt) Temp	285 到 305	°C
Mold Temperature	65 到 95	°C
Drying Time	4.0	hr
Rear Temperature	280 到 310	°C
Middle Temperature	280 到 310	°C
Front Temperature	280 到 310	°C
Nozzle Temperature	280 到 310	°C
Suggested Max Regrind	25	%

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	70	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	80	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	700	°C
	Glow Wire Flammability Index	1.5 mm	IEC 60695-2-12	700	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0 mm	IEC 60695-2-12	875	°C
Glow Wire Ignition Temperature	0.75 mm	IEC 60695-2-13	725	°C
	Glow Wire Ignition Temperature	1.5 mm	IEC 60695-2-13	725	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	750	°C
Burning Rate	2.00 mm, 自动灭火	ISO 3795	0.0	mm/min
Flame Rating	0.75 mm	UL 94	HB
	Flame Rating	1.5 mm	UL 94	HB
	Flame Rating	Flame Rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.