PA66 Zytel® 70G30HSLR NC010 DUPONT USA
118
- Unit Price:
- $3046 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Lubricity Hydrolysis resistance
- Application Areas:Electrical tools Electrical field Electrical appliances Electronic field Automotive sector
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 6.0 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.9 | % | |
| MediumDensity | 1.20 | g/cm³ | ||
| Ejection Temperature | 210 | °C | ||
| SpecificHeatCapacityofMelt | 2290 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2 | 10000 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 200 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.3 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.6E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.3E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1.1E-07 | m²/s | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 261 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 253 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 250 | °C | |
| Melting Temperature | ISO11357-3 | 262 | °C | |
| Glass Transition Temperature | ISO11357-2 | 80.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 7E-03 | |
| 1MHz | IEC60250 | 0.015 | ||
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Relative Permittivity | 100Hz | IEC60250 | 4.30 | |
| 1MHz | IEC60250 | 4.10 | ||
| Comparative Tracking Index | IEC60112 | 450 | V | |
| Comparative Tracking Index | 3.00mm | UL746 | PLC1 | |
| Dielectric Strength | IEC60243-1 | 38 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 80 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 24 | % | |
| FMVSS Flammability | FMVSS302 | SE/B | ||
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 3E-04 | g | |
| Burning Rate | 1.00mm | ISO3795 | 24 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 3.20 | µgC/g | |
| Odor | VDA270 | 4.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.