PA66 Zytel® 70G25HSLR NC010 DUPONT SHENZHEN

142

Unit Price:
$3880 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
104.1MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High rigidity High temperature resistan
Application Areas:Electrical applications Fitness equipment Automotive Applications
Color:--
Grade:Enhanced level

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	1.1	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.30	%
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.4	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0	%
Flow Length	2.00 mm		350	mm
Stickiness number		ISO 307	150	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress		ISO 178	260	Mpa
Tensile stress	Break	ISO 527-2	180	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
Tensile modulus		ISO 527-2	8500	Mpa
Bending modulus		ISO 178	8000	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	261	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	252	°C
Vicat softening temperature		ISO 306/B50	257	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	3.3E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4	cm/cm/°C
Glass transition temperature 3		ISO 11357-2	80.0	°C
Melting temperature 3		ISO 11357-3	262	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	100 Hz	IEC 62631-2-1	3.60
Leakage Trace Index		IEC 60112	400	V
Dissipation factor	100 Hz	IEC 62631-2-1	7.0E-3
Surface resistivity		IEC 62631-3-2	--	ohms
Volume resistivity		IEC 62631-3-1	1.0E+13	ohms·m

Filling analysis	Test Method	Test Result	Unit
Melt density		1.15	g/cm³
Top out temperature		210	°C
Specific Heat Capacity of Melt		2090	J/kg/°C
Thermal Conductivity of Melt		0.21	W/m/K
Odor	VDA 270	3.50

injection	Test Condition	Test Method	Test Result	Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 到 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			285 到 305	°C
Melt Temperature, Optimum			295	°C
Mold temperature			70 到 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 到 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness	H 961/30	ISO 2039-1	260	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate	1.00 mm	ISO 3795	26	mm/min
UL flame retardant rating	1.5 mm	UL 94, IEC 60695-11-10, -20	HB
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94, IEC 60695-11-10, -20	HB
FMVSS flammability		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	5.0E-4	g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.