Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.60 | |
Modeling Shrinkage | | ASTM D955 | 0.3~0.7 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Ejection Temperature | | | 210 | °C |
Modeling Shrinkage | TD | ISO294-4 | 0.70 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.30 | % |
Modeling Shrinkage | Across Flow | ISO 294-4 | 0.80 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.30 | % |
Moisture Absorption | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 158 | Mpa |
Tensile Stress | Break | ISO 527-2 | 170 | Mpa |
Tensile Strain | Break | ISO 527-2 | 2.6 | % |
Tensile Strain | Break | ISO527-2 | 2.1 | % |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 2.1 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 10640 | kg/cm²(MPa)[Lb/in²] |
Tensile Modulus | | ISO 527-2 | 10200 | Mpa |
Tensile Modulus | | ISO527-2 | 10600 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 158 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790/ISO 178 | 9410 | kg·cm/cm(J/M)ft·lb/in |
Flexural Modulus | | ISO178 | 9410 | Mpa |
Izod notch impact strength | | ASTM D256/ISO 179 | 8.4 | kg·cm/cm(J/M)ft·lb/in |
Izod notch impact strength | | ASTM D256/ISO 179 | 7.9 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO11357-3 | 260 | °C |
Melting Temperature | | ISO 11357-3 | 262 | °C |
Burning Rate | | UL94 | V-0 | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 242 | ℃(℉) |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 242 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 240 | °C |
Melting Temperature | | | 260 | ℃(℉) |
Linear thermal expansion coefficient | MD:-- | ISO11359-2 | 2.1E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:-40to23°C | ISO11359-2 | 2.5E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:55to160°C | ISO11359-2 | 1.2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-- | ISO11359-2 | 7.9E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to23°C | ISO11359-2 | 6.9E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:55to160°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 2.00 mm | IEC 60243-1 | 24 | KV/mm |
Surface Resistivity | | IEC 62631-3-2 | -- | ohms |
Volume Resistivity | | IEC 62631-3-1 | > 1.0E+13 | ohms·m |
Comparative Tracking Index | | IEC 60112 | 275 | V |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 80 | °C |
Drying time - Hot air dryer | | | 2.0 到 4.0 | hr |
Suggested Max Moisture | | | 0.20 | % |
Processing (Melt) Temp | | | 280 到 300 | °C |
Melt Temperature, Optimum | | | 290 | °C |
Mold Temperature | | | 70 到 120 | °C |
Mold Temperature, Optimum | | | 100 | °C |
Holding Pressure | | | 50.0 到 100 | Mpa |
Holding Pressure | Drying Recommended | | yes | |
Hold Pressure Time | | | 3.00 | s/mm |
Maximum Screw Tangential Speed | | | 12 | m/min |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -40°C | ISO 179/1eU | 50 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 50 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 60 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.75mm | UL94 | V-0 | |
UL flame retardant rating | 1.5mm | UL94 | V-05VA | |
UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | V-0 | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | V-05VA | |
Oxygen Index | | ISO4589-2 | 35 | % |
Flame Rating | 0.75 mm | UL 94, IEC 60695-11-10, -20 | V-0 | |
Flame Rating | 1.5 mm | UL 94, IEC 60695-11-10, -20 | V-0 5VA | |
FMVSS Flammability | | FMVSS302 | B | |
Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
EmissionofOrganicCompounds | | VDA277 | 4.70 | µgC/g |
Odor | | VDA270 | 4.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.