PA66 Zytel® 70G13L NC010 DUPONT USA
153
- Unit Price:
- $3946 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced high strength High rigidity High temperature resistan
- Application Areas:Electrical field Electrical appliances Electronic field Fitness equipment Automotive sector sporting goods
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.23 | ||
| Molding shrinkage rate | ASTM D955 | 0.7~1.2 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 2.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.2 | % |
| MD | ISO294-4 | 0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 1.7 | % |
| Saturation,23°C,2.00mm | ISO62 | 7.6 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 2.2 | % | |
| Top out temperature | 210 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| abrasion resistance | ISO4649 | 10.0 | mm³ | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.0 | % |
| Bending stress | ISO178 | 190 | Mpa | |
| elongation at break | ASTM D638/ISO 527 | 3 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 5500 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 5500 | Mpa | ||
| tensile strength | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 4900 | kg·cm/cm(J/M)ft·lb/in | |
| ISO178 | 4800 | Mpa | ||
| bending strength | ASTM D790/ISO 178 | 190 | kg·cm/cm(J/M)ft·lb/in | |
| Charpy impact strength | ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 32 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 4.5 (-40℃) | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 258 | ℃（℉） | |
| ASTM D648/ISO 75 | 238 | ℃（℉） | ||
| 0.45MPa,Unannealed | ISO75-2/B | 258 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 238 | °C | |
| melting point | 262 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.77 | mm/mm.℃ | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 4E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 4.2E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 2.6E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 9.3E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7.7E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| Glass transition temperature 2 | ISO11357-2 | 80.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 205 | °C | |
| Melting temperature 2 | ISO11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | IEC60250 | 0.013 | |
| 1MHz | IEC60250 | 0.015 | ||
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.20 | ||
| Dielectric strength | IEC60243-1 | 25 | KV/mm | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | -30°C | ISO180/1U | 35 | kJ/m² |
| 23°C | ISO180/1U | 40 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.71mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 24 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | 27 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 6.00 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.