PA66 Amilan® CM3001G30 TORAY JAPAN
229
- Unit Price:
- $3971 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:OA device Electrical components Electrical appliances Automotive sector Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.60 | % |
| Saturation, 23°C | ISO 62 | 5.5 | % | |
| density | 23°C | ISO 1183 | 1.37 | g/cm³ |
| Shrinkage rate 3 | Across Flow : 3.00 mm | 内部方法 | 0.60 到 0.90 | % |
| 流量 : 3.00 mm | 内部方法 | 0.20 到 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber abraser | 1000 Cycles | ISO 9352 | 0.400 | mg |
| Tensile stress | -40°C | ISO 527-2 | 235 | Mpa |
| 23°C | ISO 527-2 | 190 | Mpa | |
| 80°C | ISO 527-2 | 120 | Mpa | |
| Tensile strain | Break, -40°C | ISO 527-2 | 2.0 | % |
| Break, 23°C | ISO 527-2 | 2.5 | % | |
| Break, 80°C | ISO 527-2 | 5.0 | % | |
| Bending modulus | -40°C | ISO 178 | 11600 | Mpa |
| 23°C | ISO 178 | 9500 | Mpa | |
| 80°C | ISO 178 | 5800 | Mpa | |
| Bending stress | -40°C | ISO 178 | 325 | Mpa |
| 23°C | ISO 178 | 290 | Mpa | |
| 80°C | ISO 178 | 190 | Mpa | |
| Compressive stress | -40°C | ISO 604 | 250 | Mpa |
| 23°C | ISO 604 | 180 | Mpa | |
| 80°C | ISO 604 | 110 | Mpa | |
| shear strength | 23°C | ASTM D732 | 95.0 | Mpa |
| Friction coefficient - vs. Metal 4 | Suzuki Method | 0.15 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 262 | °C |
| specific heat | 1800 | J/kg/°C | ||
| thermal conductivity | 0.40 | W/m/K | ||
| Melting temperature | DSC | 265 | °C | |
| Linear coefficient of thermal expansion - flow | ISO 11359-2 | 2.0E-5 到 3.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+13 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 20 | KV/mm | |
| Dielectric constant 5 | 23°C, 50 Hz | IEC 60250 | 4.60 | |
| 23°C, 1 kHz | IEC 60250 | 4.40 | ||
| 23°C, 1 MHz | IEC 60250 | 3.90 | ||
| Dissipation factor 5 | 23°C, 50 Hz | IEC 60250 | 0.020 | |
| 23°C, 1 kHz | IEC 60250 | 0.020 | ||
| 23°C, 1 MHz | IEC 60250 | 0.020 | ||
| Arc resistance 6 | UL 746 | 114 | sec |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO 179 | 10 | kJ/m² |
| 23°C | ISO 179 | 13 | kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 60 | kJ/m² |
| 23°C | ISO 179 | 65 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M -Sale, 23°C | ISO 2039-2 | 97 | |
| R -Sale, 80°C | ISO 2039-2 | 24 | ||
| R -Sale, 23°C | ISO 2039-2 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.79 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.