Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:23°C,2.00mm | ISO294-4 | 0.90 | % |
Modeling Shrinkage | MD:23°C,2.00mm | ISO294-4 | 0.40 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.80 | % |
Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 1.7 | % |
Density | | ISO1183 | 1.40 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 23°C | ISO527-2 | 10600 | Mpa |
Flexural Modulus | 23°C | ISO178 | 10200 | Mpa |
Flexural Stress | 23°C | ISO178 | 290 | Mpa |
Tensile Stress | 断裂,23°C | ISO527-2 | 205 | Mpa |
Tensile Strain | 断裂,23°C | ISO527-2 | 3.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | 0.75mm | UL746 | 140 | °C |
RTIElec | 1.5mm | UL746 | 140 | °C |
RTIElec | 3.0mm | UL746 | 140 | °C |
Evolution Calendar intelligent importer | 0.75mm | UL746 | 125 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 125 | °C |
Evolution Calendar intelligent importer | 3.0mm | UL746 | 125 | °C |
RTIStr | 0.75mm | UL746 | 140 | °C |
RTIStr | 1.5mm | UL746 | 140 | °C |
RTIStr | 3.0mm | UL746 | 140 | °C |
Linear thermal expansion coefficient | TD:23to55°C,2.00mm | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Linear thermal expansion coefficient | MD:23to55°C,2.00mm | ISO11359-2 | 2.1E-05 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 260 | °C |
Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 260 | °C |
Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 250 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1.00mm | IEC60243 | 20 | KV/mm |
Comparative Tracking Index | 3.00mm | IEC60112 | 250to399 | V |
Volume Resistivity | 0.750mm | IEC60093 | 1E+13 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 11 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180 | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180 | 12 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 80 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 70 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 0.75mm | IEC60695-2-12 | 725 | °C |
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 700 | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 875 | °C |
Glow Wire Ignition Temperature | 0.75mm | IEC60695-2-13 | 750 | °C |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 725 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 750 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.