PA66 Leona™ 14G33 ASAHI JAPAN

214

Unit Price:
$3620 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability Moderate heat resistance Creep resistance Fatigue resistance high strength High rigidity
Application Areas:Electrical field Electronic field Engine hood parts component Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	内部方法	0.80	%
	Modeling Shrinkage	MD	内部方法	0.40	%
	Modeling Shrinkage	Modeling Shrinkage	干	旭化成方法	0.4/0.8	%
Taber Abrasion Resistance	湿	ASTM D-1044	15	×10-6kg/1000times

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	10.4(6.3)	GPa
Tensile Stress	Break,23°C	ISO527-2	208	Mpa
Tensile Strain	Break,23°C	ISO527-2	4.0	%
Tensile Strength		ASTMD638	210	Mpa
Flexural Stress	23°C	ISO178	302	Mpa
Tensile Strength	干(湿)	ASTM D-790	325(210)	Mpa
Elongation at break	干(湿)	ASTM D-638	3(5)	%
Notched Izod Impact Strength	干(湿)	ASTM D-256	130(170)	J/m
Tensile Modulus	23°C	ISO527-2	9800	Mpa
Tensile Strength	干(湿)	ASTM D-638	210(135)	Mpa
Tensile Elongation	Break	ASTMD638	3.0	%
Rockwell Hardness	干(湿)	ASTM D-785	96(75)	M Scale
Rockwell Hardness	Rockwell Hardness	干(湿)	ASTM D-785	120(-)	R scale
Flexural Modulus		ASTMD790	10400	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	9600	Mpa
Flexural Strength		ASTMD790	325	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	250	°C
	Deflection Temperature Under Load?	0.46MPa,干	ASTM D-648	260	°C
		Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	260	°C
			Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	260	°C
				Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	250	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	250	°C
Linear expansion coefficient	干	ASTM D-696	2	×10-5/K
Thermal Conductivity	干		0.3	W/(m.K)
Linear thermal expansion coefficient	MD	ASTMD696	2E-05	cm/cm/°C
Flame retardancy	干	UL 94	HB
Thermal Conductivity			0.30	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	3.00mm	IEC60112	425	V
Dielectric Strength		ASTMD149	33	KV/mm
Dielectric Strength	Dielectric Strength		IEC60243-1	33	KV/mm
Surface Resistivity		ASTMD257	1E+15	ohms
Surface Resistivity	Surface Resistivity		IEC60093	1E+15	ohms
Volume Resistivity		ASTMD257	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	90	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ASTMD785	96
	Rockwell Hardness	R-Sale	ASTMD785	120
		Rockwell Hardness	M-Sale	ISO2039-2	96
		Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	120

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		1.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.