PA66 Ultramid® A3X2G7 BASF GERMANY
212
- Unit Price:
- $6028 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Electrical performance Flame retardant high strength High rigidity Oil resistant
- Application Areas:Electrical applications Electrical components
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.34 | % | |
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 25.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break,23°C | ISO527-2 | 160 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| elongation at break | ASTM D638/ISO 527 | 160/120 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 9200 | kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO527-2 | 11000 | Mpa | |
| tensile strength | ASTM D638/ISO 527 | 160/120 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 3/4 | % | |
| Bending modulus | 23°C | ISO178 | 9200 | Mpa |
| Charpy impact strength | ASTM D256/ISO 179 | 14/18 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 70/70 | kg·cm/cm(J/M)ft·lb/in | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 3/4 | % | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 13/20 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | 0.40mm | UL746 | 110 | °C |
| 0.75mm | UL746 | 115 | °C | |
| 1.5mm | UL746 | 115 | °C | |
| 3.0mm | UL746 | 115 | °C | |
| Evolution Calendar intelligent importer | 0.40mm | UL746 | 115 | °C |
| 0.75mm | UL746 | 115 | °C | |
| 1.5mm | UL746 | 115 | °C | |
| 3.0mm | UL746 | 115 | °C | |
| RTIStr | 0.75mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 130 | °C | |
| 3.0mm | UL746 | 130 | °C | |
| Linear coefficient of thermal expansion | MD | 1.7E-05 | cm/cm/°C | |
| TD | 6.5E-05 | cm/cm/°C | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 250 | ℃（℉） | |
| melting point | 220 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.5-2/6-7 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257/IEC 60093 | >1013/1010 | Ω | |
| Dielectric constant | ASTM D150/IEC 60250 | 3.6/5 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 1015/1012 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 65 | kJ/m² |
| 23°C | ISO179 | 70 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.