PA66 Ultramid® A3X2G5 BASF GERMANY
191
- Unit Price:
- $6181 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 103MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Electrical performance Flame retardant Oil resistant
- Application Areas:Electrical applications Electrical components
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.34 | ||
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 5.7-6.3 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | 干/湿 | 8500/6000 | Mpa | |
| Tensile Creep Modulus | 1000h,湿 | 3500 | Mpa | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 3/4.5 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 8500/6000 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | ASTM D638/ISO 527 | 140/100 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ≤0.5%, +23℃，湿 | 3500 | Mpa | |
| Flexural Modulus | 干/湿 | 7100 | Mpa | |
| Ball Indentation Hardness | 干/湿 | 190 | Mpa | |
| Tensile Stress (Break) | 干/湿 | 140/100 | Mpa | |
| Notched Izod Impact Strength | +23℃，干/湿 | 13/17 | KJ/m | |
| Notched Izod Impact Strength | +23℃，干/湿 | 4/10 | J | |
| Notched Izod Impact Strength | +23℃，干/湿 | 65/70 | KJ/m | |
| 30℃，干 | 60 | KJ/m | ||
| Tensile Elongation (Yield, 50mm/min) | 干/湿 | 3/4.5 | % | |
| Tensile Stress (Yield 50mm/min) | 干/湿 | 140/100 | Mpa | |
| Notched Izod Impact Strength | +23℃，干/湿 | 11/17 | KJ/m | |
| Tensile Elongation (Break, 50mm/min) | 干/湿 | 3/4.5 | % | |
| Charpy impact strength | ASTM D256/ISO 179 | 13/17 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa负荷，Dry | 250 | °C | |
| 0.45MPa负荷，Dry | 250 | °C | ||
| ASTM D648/ISO 75 | 250 1.8Mpa | ℃（℉） | ||
| Melting Temperature | 260 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 2.5-3.5/6-8 | mm/mm.℃ | |
| Thermal Conductivity | Dry | 0.27 | W/(m.K) | |
| Specific Heat | Dry | 1.5 | J/(g.K) | |
| Coefficient of Linear Thermal Expansion | （23-80）℃，Dry | 2.5-3.5/6-8 | ||
| Continuous Use Temperature | 220 | °C | ||
| Temperature Index | 在20000h/5000h，后拉伸强度下降50%时 | 139/157 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistance | 干/湿 | >10 | Ω | |
| Taber Abrasion Resistance | 1MHz，干/湿 | 0.02/0.1 | ||
| Comparative Tracking Index | 干/湿 | CTI 500 | ||
| Comparative Tracking Index | 干/湿 | CTI 525 M | ||
| Surface Resistivity | ASTM D257/IEC 60093 | 10^13/10^10 | Ω | |
| Dielectric Constant | 1MHz，干/湿 | 3.7/5 | ||
| Volume Resistivity | ASTM D257/IEC 60093 | 10^15/10^12 | Ω.cm | |
| Dielectric Strength | K20/P50，干/湿 | 80/65 | KV/mm | |
| Volume Resistivity | 干/湿 | 10 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Other Prices
| Port of Loading | Unit Price |
|---|---|
| Huangpu port, China | 5842 USD/MT |