PA66 Ultramid® A3EG10 BASF GERMANY
128
- Unit Price:
- $3071 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 51MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant High rigidity
- Application Areas:Electronic insulation Industrial components
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1560 | ||
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 3.7-4.3 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 23℃,50%相对湿度 | % | ISO 62 | |
| Modeling Shrinkage | 23℃ | % | 0.10到0.31 | |
| Melting Temperature | ℃ | ISO 3146 | ||
| Melt Volume flow Rate | cm | ISO 1133 | ||
| Saturation ,23℃ | % | 3.5到5.0 | ||
| Flow,23℃,50%RH | % | 1.2到1.5 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | KJ/m | ISO 179/1eA | 18 | |
| Tensile Stress | Break,23℃ | MPa | 144.83到292.41 | |
| Tensile Strain | Break,23℃ | % | 1.9到3.1 | |
| Tensile Modulus | ASTM D638/ISO 527 | 16800 | kg/cm²(MPa)[Lb/in²] | |
| MPa | ISO 527-2 | |||
| 23℃ | MPa | 8206.9到28000.0 | ||
| Flexural Modulus | MPa | ISO 178 | ||
| ASTM D790/ISO 178 | 15000 | kg·cm/cm(J/M)ft·lb/in | ||
| Flexural Strength | ASTM D790/ISO 178 | 360 | kg·cm/cm(J/M)ft·lb/in | |
| IZOD Notch Impact Strength | KJ/m | ISO 180/1A | ||
| Tensile Stress (Yield) | MPa | ISO 527-2 | 230 | |
| Izod notch impact strength | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | °C | 260 | ||
| Flame retardancy | UL94 | HB | ||
| Continuous Use Temperature | °C | 110到220 | ||
| 8.0Mpa, Unannealed | °C | 65到220 | ||
| Flow | mm/mm/°C | 68.6E-5到127.0E-5 | ||
| Flow | mm/mm/°C | 142.2E-5到203.2E-5 | ||
| Deflection Temperature Under Load? | -，0.45Mpa | ℃ | ISO 75-2 | 250 |
| -，1.8Mpa | ℃ | ISO 75-2 | 250 | |
| Melting Temperature | 260 | ℃（℉） | ||
| 1.8MPa, Unannealed | °C | 230到250 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 23℃ | V/mil | 840 | |
| Surface Resistivity | Ω | IEC 60093 | ||
| Dielectric Constant | 1MHz | IEC 60250 | 3.8 | |
| Volume Resistivity | ASTM D257/IEC 60093 | 1E 13 | Ω.cm | |
| Ω.M | IEC 60093 | |||
| 23℃ | ohms·cm | 1.0E+12到1.0E+14 | ||
| Dielectric loss | 1MHz | IEC 60250 | 0.015 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 11.143到19.964 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | MPa | 222.76到370.34 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.