Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.18 | |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | | UL 94 | 113 | |
| Modeling Shrinkage | MD：1.00mm3 | % | 0.60到0.90 | |
| Modeling Shrinkage | MD：3.00mm4 | % | 1.0到1.6 | |
| Moisture Absorption | 23°C,24hr | % | 1.1 | -- |
| Moisture Absorption | Saturation,23°C | % | 7.5 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 23°C | MPa | 85.0 | 65.0 |
| Tensile Stress | 80°C | MPa | 45.0 | -- |
| Tensile Strain | Break,23°C | % | 7.5 | 7.5 |
| Flexural Modulus | 23°C | MPa | 3500 | 1500 |
| Flexural Modulus | 80°C | MPa | 1200 | -- |
| Flexural Stress | -40°C | MPa | 170 | -- |
| Flexural Stress | 23°C | MPa | 125 | 70.0 |
| Flexural Stress | 80°C | MPa | 65.0 | -- |
| Tensile Strength (Yield) | 23°C | ASTM D-638 | 850 | kg/cm |
| Tensile Strength (Break) | 23°C | ASTM D-638 | 12 | kg/cm |
| Taber Abrasion Resistance | 1000Cycles | mg | 9.00到10.0 | -- |
| Flexural strength | -40°C | ASTM D-790 | 1210 | kg/cm |
| Flexural Modulus | -40°C | ASTM D-790 | 34500 | kg/cm |
| Notched Izod Impact Strength | Unnotched1/2" 23°C | | 5 | kg.cm/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | °C | 265 | -- |
| Deflection Temperature Under Load | 4.6kg/cm | ASTM D-648 | 244 | °C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | °C | 244 | -- |
| Melting Temperature | | 差示扫描测热计DSC法 | 265 | °C |
| Melting Temperature | | | 265 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Arc Resistance | 1/8" | ASTM D-150 | 127 | |
| Dielectric Constant | 23°C,50Hz | | 5.20 | -- |
| Dissipation Factor | 23°C,50Hz | | 0.070 | -- |
| Arc Resistance | | sec | 127 | -- |
| Comparative Tracking Index | 导热率温度指表 | UL 746 | 600 | V |
| Comparative Tracking Index | CTI | V | 600 | -- |
| Volume Resistivity | | ohms·cm | 1E+15 | -- |
| Volume Resistivity | | ASTM D-257 | V-0 | Ω.cm |
| Dielectric Strength | 1/8" 短时间 | ASTM D-149 | 17 | KV/mm |
| Dielectric Strength | | kV/mm | 28 | -- |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -40°C | kJ/m² | 140 | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | | 120 | -- |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.40mm | | V-0 | -- |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | （24hr）23°C | ASTM D-570 | 1.1 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.