PA66 Leona™ FG172 ASAHI JAPAN

180

Unit Price:
$4413 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Thermal stability
Application Areas:Electrical field Electrical components Electronic field switch Connector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	内部方法	0.90	%
	Modeling Shrinkage	MD	内部方法	0.40	%
	Modeling Shrinkage	Modeling Shrinkage	干	旭化成方法	0.4-0.9	%
Taber Abrasion Resistance	湿	ASTM D-1044	24	×10-6kg/1000times

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	7.6(5.9)	GPa
Elongation at break	干(湿)	ASTM D-638	2.5(2.7)	%
Notched Izod Impact Strength	干(湿)	ASTM D-256	63(72)	J/m
Flexural Stress	23°C	ISO178	208	Mpa
Tensile Strength	干(湿)	ASTM D-790	216(177)	Mpa
Tensile Stress	Break,23°C	ISO527-2	136	Mpa
Tensile Strain	Break,23°C	ISO527-2	2.5	%
Tensile Strength		ASTMD638	153	Mpa
Tensile Modulus	23°C	ISO527-2	9100	Mpa
Tensile Strength	干(湿)	ASTM D-638	153(123)	Mpa
Tensile Elongation	Break	ASTMD638	2.5	%
Rockwell Hardness	干(湿)	ASTM D-785	95(55)	M Scale
Flexural Modulus		ASTMD790	7600	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	8000	Mpa
Flexural Strength		ASTMD790	216	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	255	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	256	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	240	°C
			Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	248	°C
				Deflection Temperature Under Load?	0.46MPa,干	ASTM D-648	255	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	248	°C
Linear expansion coefficient	干	ASTM D-696	3	×10-5/K
Linear thermal expansion coefficient	MD	ASTMD696	3E-05	cm/cm/°C
Flame retardancy	干	UL 94	V-0

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	3.00mm	IEC60112	250	V
Dielectric Strength		ASTMD149	28	KV/mm
Dielectric Strength	Dielectric Strength		IEC60243-1	28	KV/mm
Surface Resistivity		ASTMD257	1E+14	ohms
Surface Resistivity	Surface Resistivity		IEC60093	1E+14	ohms
Volume Resistivity		ASTMD257	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	64	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTMD785	95
Rockwell Hardness	Rockwell Hardness	M-Scale	ISO2039-2	95

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	V-0
Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C
Oxygen Index		ASTMD2863	37	%

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		0.9	%

Other performance	Test Condition	Test Method	Test Result	Unit
Oxygen Index	干	ASTM D-2863	37	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.