Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.25 | |
Modeling Shrinkage | | ASTM D955 | 0.7-1.2 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 2.1 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | 干 | 旭化成方法 | 0.7/1.2 | % |
Taber Abrasion Resistance | 湿 | ASTM D-1044 | 9 | ×10-6kg/1000times |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | 干(湿) | ASTM D-790 | 4.9(2.5) | GPa |
Tensile Strength | 干(湿) | ASTM D-790 | 167(108) | Mpa |
Elongation at break | 干(湿) | ASTM D-638 | 2.5(8) | % |
Notched Izod Impact Strength | 干(湿) | ASTM D-256 | 49(59) | J/m |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 2.5 | % |
Tensile Strength | 干(湿) | ASTM D-638 | 108(79) | Mpa |
Rockwell Hardness | 干(湿) | ASTM D-785 | 94(71) | M Scale |
Rockwell Hardness | 干(湿) | ASTM D-785 | 120(-) | R scale |
Flexural Modulus | | ASTM D790/ISO 178 | 4900 | kg·cm/cm(J/M)ft·lb/in |
Flexural Strength | | ASTM D790/ISO 178 | 167 | kg·cm/cm(J/M)ft·lb/in |
Charpy impact strength | | ASTM D256/ISO 179 | 49 | kg·cm/cm(J/M)ft·lb/in |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 107.9 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | HB | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 240 | ℃(℉) |
Deflection Temperature Under Load? | 0.46MPa,干 | ASTM D-648 | 258 | °C |
Deflection Temperature Under Load? | 1.82MPa,干 | ASTM D-648 | 240 | °C |
Linear expansion coefficient | 干 | ASTM D-696 | 4 | ×10-5/K |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 4 | mm/mm.℃ |
Flame retardancy | 干 | UL 94 | HB | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Arc Resistance | | ASTM D495/IEC 60112 | 142 | |
Volume Resistivity | | ASTM D257/IEC 60093 | 10 | Ω.cm |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 湿 | | 2.1 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.