Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.4 | % |
| Modeling Shrinkage | TD:80°C,48hr | ISO294-4 | 0.10 | % |
| Modeling Shrinkage | MD | ISO294-4 | 1.4 | % |
| Modeling Shrinkage | MD:80°C,48hr | ISO294-4 | 0.20 | % |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 8.5 | % |
| Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 2.6 | % |
| MediumDensity | | | 0.970 | g/cm³ |
| Ejection Temperature | | | 190 | °C |
| SpecificHeatCapacityofMelt | | | 2790 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.16 | W/m/K |
| Density / Specific Gravity | | ISO1183 | 1.14 | g/cm³ |
| Viscosity number | | ISO307 | 140 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | -- | Mpa |
| Nominal Tensile Strain at Break | | ISO527-2 | 20 | % |
| Tensile Stress | Yield | ISO527-2 | 82.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 4.5 | % |
| Tensile Creep Modulus | 1000hr | ISO899-1 | -- | Mpa |
| Tensile Modulus | | ISO527-2 | 3100 | Mpa |
| Flexural Modulus | | ISO178 | 2800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 190 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Glass Transition Temperature | | ISO11357-2 | 60.0 | °C |
| Effective Thermal Diffusivity | | | 5E-08 | m²/s |
| Vicat Softening Temperature | | ISO306/B50 | 240 | °C |
| Melting Temperature | | ISO11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 100Hz | IEC60250 | 0.014 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.018 | |
| Relative Permittivity | 100Hz | IEC60250 | 3.80 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.60 | |
| Dielectric Strength | | IEC60243-1 | 32 | KV/mm |
| Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strain (MD) | Yield | ISO527-3 | 4.5 | % |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 5.5 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 6.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 5.5 | kJ/m² |
| Notched Izod impact strength | -30°C | ISO180/1U | 300 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO180/1U | 300 | kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 400 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
| UL flame retardant rating | 0.71mm | IEC60695-11-10,-20 | V-2 | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | V-2 | |
| Oxygen Index | | ISO4589-2 | 28 | % |
| FMVSS Flammability | | FMVSS302 | SE | |
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 6.50 | µgC/g |
| Odor | | VDA270 | 3.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.