Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 1.35 | g/cm³ |
Modeling Shrinkage | TD:260℃,2.0 mm Across Flow : 500°F, 0,0787 in 3 3 | ISO 2577 | 1.1 | % |
Modeling Shrinkage | TD:120℃,2.0 mm,4 hrs Across Flow : 248°F, 4 hr, 0,0787 in 4 4 | ISO 2577 | 0.4 | % |
Modeling Shrinkage | MD:260℃,2.0 mm Flow : 500°F, 0,0787 in 3 3 | ISO 2577 | 1.1 | % |
Modeling Shrinkage | MD:120℃,2.0 mm,4 hrs Flow : 248°F, 4 hr, 0.0787 in 4 4 | ISO 2577 | 0.4 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strain | Yield,23℃ | ISO 527-2/50 | 3.7 | % |
Flexural Strength | 3.50% Strain,23℃ 3.5% Strain, 23°C | ISO 178-A | 100 | Mpa |
Flexural Strength | 23℃ 23°C 5 5 | ISO 178-A | 110 | Mpa |
Flexural Modulus | 23℃ 23℃ 5 | ISO 178-A | 3200 | Mpa |
Tensile Modulus | 23℃ 23℃ | ISO 527-1-2 | 3600 | Mpa |
Tensile Strength | Yield,23℃ | ISO 527-2/50 | 70 | Mpa |
Nominal Tensile Strain at Break | 23℃ 23℃ | ISO 527-2/50 | 9 | % |
Electrical | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | Solution A | IEC 60112 | 300 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | -30℃ -30°C | ISO 180/1U | 100 | kJ/m² |
Unnotched Izod Impact Strength | 23℃ 23°C | ISO 180/1U | 120 | kJ/m² |
Charpy Notched Impact Strength | -30℃ -30°C | ISO 179/1eA | < 10 | kJ/m² |
Charpy Notched Impact Strength | 23℃ 23°C | ISO 179/1eA | < 10 | kJ/m² |
Notched Izod Impact Strength | -30℃ -30°C | ISO 180-1A | < 10 | kJ/m² |
Notched Izod Impact Strength | 23℃ 23°C | ISO 180-1A | < 10 | kJ/m² |
Charpy Unnotched Impact Strength | -30℃ -30°C | ISO 179/1eU | 130 | kJ/m² |
Charpy Unnotched Impact Strength | 23℃ 23°C | ISO 179/1eU | 150 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.40 mm 0.40 mm | UL 94 | V-0 | |
Flame Rating | 0.75 mm 0.75 mm | UL 94 | V-0 | |
Flame Rating | 1.50 mm 1.5 mm | UL 94 | V-0 | |
Flame Rating | 2.00 mm 2.0 mm | UL 94 | 5VA | |
Flame Rating | 3.00 mm 3.0 mm | UL 94 | 5VA | |
Glow Wire Flammability Index | 0.80 mm 0.8 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 1.5 mm 1.5 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 3.0 mm 3.0 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 0.75 mm 0.75 mm | IEC 60695-2-13 | 825 | °C |
Glow Wire Ignition Temperature | 1.5 mm 1.5 mm | IEC 60695-2-13 | 825 | °C |
Glow Wire Ignition Temperature | 3 mm 3.0 mm | IEC 60695-2-13 | 800 | °C |
Thermal | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO 11357-3 | 222 | °C |
Heat Deflection Temperature | 1.8 MPa,Unannealed | ISO 75-2/A | 70 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.