Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Viscosity number | | ISO307 | 145 | cm³/g |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1A/1 | 11000 | Mpa |
Tensile Stress | Break | ISO527-2/1A/5 | 180 | Mpa |
Tensile Strain | Break | ISO527-2/1A/5 | 3.4 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/Bf | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 210 | °C |
Ball PressureTest | 150°C | IEC60695-10-2 | Pass | |
Vicat Softening Temperature | | ISO306/B50 | 210 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | IEC60112 | 450 | V |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+13 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 70 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 90 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H358/30 | ISO2039-1 | 230 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | -- | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | -- | °C |
Burning Rate | | ISO3795 | <30 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.