Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.18mm | | 0.90 | % |
Moisture Absorption | 24hr | ASTMD570 | 1.1 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 1.1 | % |
Moisture Absorption | Saturation | ASTMD570 | 5.7 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 5.7 | % |
Moisture Absorption | Equilibrium,50%RH | ASTMD570 | 1.6 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 1.6 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break,23°C | ISO527-2 | 85.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 10 | % |
Flexural Stress | 23°C | ISO178 | 140 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 6400 | Mpa |
Tensile Modulus | 80°C | ISO527-2 | 1360 | Mpa |
Tensile Modulus | 120°C | ISO527-2 | 970 | Mpa |
Tensile Modulus | 150°C | ISO527-2 | 910 | Mpa |
Tensile Modulus | -40°C | ISO527-2 | 8310 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 10 | % |
Flexural Modulus | -40°C | ASTMD790 | 5860 | Mpa |
Flexural Modulus | 23°C | ASTMD790 | 5760 | Mpa |
Flexural Modulus | 65°C | ASTMD790 | 1540 | Mpa |
Flexural Modulus | 90°C | ASTMD790 | 810 | Mpa |
Flexural Modulus | 121°C | ASTMD790 | 815 | Mpa |
Flexural Modulus | 23°C | ISO178 | 5200 | Mpa |
Flexural Strength | -40°C | ASTMD790 | 207 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 138 | Mpa |
Flexural Strength | 65°C | ASTMD790 | 55.0 | Mpa |
Flexural Strength | 90°C | ASTMD790 | 35.0 | Mpa |
Flexural Strength | 121°C | ASTMD790 | 34.0 | Mpa |
Tensile Strength | Break,23°C | ASTMD638 | 90.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 195 | °C |
Peak Melting Temperature | | ASTMD3418 | 220 | °C |
Linear thermal expansion coefficient | MD | ASTME831 | 5E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD | | 4.6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | | 5.8E-05 | cm/cm/°C |
Melting temperature (DSC) | | ISO3146 | 220 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | 1.50mm | ASTMD257 | >1.0E+15 | ohms·cm |
Dielectric Strength | 1.50mm | ASTMD149 | 22 | KV/mm |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 120 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 119 | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
DropWeightImpactStrength | 23°C | 内部方法 | 6.78 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.