PA6 Ultramid® B3GK24 BK00564 BASF GERMANY
155
- Unit Price:
- $4482 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Oil resistant Filler: glass beads fibe 30% filler by weight
- Application Areas:Thin walled components Electrical enclosure Industrial components Application in the automo Plastic accessories Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation | ASTMD570 | 6.6 | % |
| Saturation,23°C | ISO62 | 6.6 | % | |
| Equilibrium,50%RH | ASTMD570 | 2.0 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 2.0 | % | |
| Modeling Shrinkage | MD：3.18mm | 0.40 | % | |
| Melt Volume flow Rate | 275°C/5.0kg | ISO1133 | 70.0 | cm3/10min |
| Density / Specific Gravity | ASTMD792 | 1.34 | g/cm³ | |
| ISO1183 | 1.34 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress (Yield 50mm/min) | 干/湿 | 110/65 | Mpa | |
| Notched Izod Impact Strength | +23℃，干/湿 | 5/8.5 | KJ/m | |
| Tensile Elongation (Break, 50mm/min) | 干/湿 | 3.5/15 | % | |
| Ball Indentation Hardness | 干/湿 | 170/120 | Mpa | |
| Tensile Stress (Break) | 干/湿 | 110/65 | Mpa | |
| Notched Izod Impact Strength | 30℃，干/湿 | 5 | KJ/m | |
| Notched Izod Impact Strength | +23℃,干/湿 | 40/90 | KJ/m | |
| 30℃干 | 39 | KJ/m | ||
| Tensile Elongation (Yield, 50mm/min) | 干/湿 | 3.5/15 | % | |
| Tensile Modulus | 干/湿 | 6000/3000 | Mpa | |
| Tensile Creep Modulus | 1000h,湿 | 2000 | Mpa | |
| Tensile Strength | Break,23°C | ASTMD638 | 110 | Mpa |
| Tensile Stress | Break,23°C | ISO527-2 | 105 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 3.5 | % |
| Tensile Modulus | 23°C | ISO527-2 | 6000 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 4830 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 215 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 215 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 200 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C | |
| 0.45MPa负荷，Dry | 215 | °C | ||
| 1.8MPa负荷，Dry | 200 | °C | ||
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| Coefficient of Linear Thermal Expansion | （23-80）℃，Dry | 3.5-4 | ||
| Peak Melting Temperature | ASTMD3418 | 220 | °C | |
| Linear thermal expansion coefficient | MD | ASTME831 | 1E-05 | cm/cm/°C |
| MD | 3.8E-05 | cm/cm/°C | ||
| RTIElec | 0.75mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 65.0 | °C | |
| 3.0mm | UL746 | 65.0 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 65.0 | °C | |
| 3.0mm | UL746 | 65.0 | °C | |
| RTIStr | 0.75mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 65.0 | °C | |
| 3.0mm | UL746 | 65.0 | °C | |
| Continuous Use Temperature | 200 | °C | ||
| Thermal Conductivity | Dry | 0.34 | W/(m.K) | |
| Specific Heat | Dry | 1.4 | J/(g.K) |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | 干/湿 | 175/100 | Mpa | |
| Surface resistance | 干/湿 | 10 | Ω | |
| Volume Resistivity | 1.50mm | ASTMD257 | 1E+15 | ohms·cm |
| Taber Abrasion Resistance | 1MHz，干/湿 | 0.02/0.07 | ||
| Comparative Tracking Index | 干/湿 | CTI 425 | ||
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 | |
| Dielectric Strength | K20/P50，干/湿 | 135/53 | KV/mm | |
| Volume Resistivity | 干/湿 | 10 | Ω.cm | |
| Comparative Tracking Index | IEC60112 | 425 | V | |
| Dielectric Constant | 1MHz | IEC60250 | 3.90 | |
| 1MHz，干/湿 | 3.9/4.6 | J/(g.K) | ||
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 39 | kJ/m² |
| 23°C | ISO179 | 40 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 5.0 | kJ/m² |
| 23°C | ISO179 | 5.0 | kJ/m² | |
| Notched Izod Impact Strength | -40°C | ASTMD256 | 32 | J/m |
| 23°C | ASTMD256 | 37 | J/m |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 干/湿 | 5/25 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.