Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:280°C,2.00mm2 | ISO294-4 | 0.81 | % |
Modeling Shrinkage | TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.10 | % |
Modeling Shrinkage | MD:280°C,2.00mm2 | ISO294-4 | 0.29 | % |
Modeling Shrinkage | MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.050 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 7.0 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 2.1 | % |
Apparent Density | | ISO60 | 0.60 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Break,23°C | ASTMD638 | 165 | Mpa |
Flexural Stress | 3.5%Strain | ISO178/A | 255 | Mpa |
Flexural Stress | 23°C | ISO178 | 260 | Mpa |
Flexural Stress | FlexuralStrainatFlexuralStrength5(23°C) | | 3.6 | % |
Flexural Modulus | 23°C | ISO178/A | 8400 | Mpa |
Tensile Stress | Break,23°C | ISO527-2/5 | 170 | Mpa |
Tensile Strain | Break,23°C | ISO527-2/5 | 3.0 | % |
Tensile Modulus | 23°C | ASTMD638 | 8730 | Mpa |
Tensile Modulus | 23°C | ISO527-2/1 | 9400 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 3.2 | % |
Flexural Modulus | 23°C | ASTMD790 | 8000 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 260 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 219 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 210 | °C |
Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 150 | °C |
Vicat Softening Temperature | | ISO306/B120 | 210 | °C |
Ball PressureTest | 210°C | IEC60695-10-2 | Pass | |
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:23to55°C | ISO11359-2 | 1E-04 | cm/cm/°C |
Melting Temperature | | ISO11357-3 | 221 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | SolutionA | IEC60112 | 400 | V |
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 33 | KV/mm |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Film Puncture Energy | --6 | ISO6603-2 | 2.10 | J |
Film Puncture Energy | --7 | ISO6603-2 | 2.20 | J |
Film Puncture Force | --6 | ISO6603-2 | 744 | N |
Film Puncture Force | --7 | ISO6603-2 | 803 | N |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180/1U | 60 | kJ/m² |
Notched Izod impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 55 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 65 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 193 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
BurningBehavior9 | | ISO3795 | passed | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
ISO Shortname | | ISO1874 | PA6,GHR,10-090,GF30 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.