PA6 Zytel® 73G30HSL DUPONT USA
159
- Unit Price:
- $1749 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 32MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability 30% filler by weight Filler: Glass fiber reinf
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 6.3 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.9 | % | |
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.20 | % | |
| MediumDensity | 1.20 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 2280 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K | ||
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Density / Specific Gravity | ISO1183 | 1.36 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO178 | 8500 | Mpa | |
| Flexural Stress | ISO178 | 280 | Mpa | |
| Tensile Creep Modulus | 1hr | ISO899-1 | -- | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | -- | Mpa |
| Tensile Stress | Break | ISO527-2 | 190 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.5 | % |
| Tensile Modulus | ISO527-2 | 9500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 210 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 215 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| Effective Thermal Diffusivity | 9.1E-08 | m²/s | ||
| Melting Temperature | ISO11357-3 | 221 | °C | |
| Glass Transition Temperature | ISO11357-2 | 60.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 3.50 | J |
| Notched Izod impact strength | 23°C | ISO180/1U | 80 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 | kJ/m² |
| 23°C | ISO179/1eU | 100 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ISO2039-2 | 121 | |
| Ball Indentation Hardness | H961/30 | ISO2039-1 | 230 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS Flammability | FMVSS302 | B | ||
| Burning Rate | 1.00mm | ISO3795 | 50 | mm/min |
| Oxygen Index | ISO4589-2 | 21 | % | |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 8.50 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.