Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Saturation,23°C | ISO62 | 9.5 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 3.0 | % |
| Density / Specific Gravity | | ISO1183 | 1.13 | g/cm³ |
| Melt Volume flow Rate | 275°C/5.0kg | ISO1133 | 175 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 10 | % |
| Tensile Modulus | 23°C | ISO527-2 | 3400 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 3000 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 90.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 4.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 65.0 | °C |
| Melting temperature (DSC) | | ISO3146 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 1MHz | IEC60250 | 0.030 | |
| Comparative Tracking Index | | IEC60112 | 600 | V |
| Dielectric Constant | 1MHz | IEC60250 | 3.30 | |
| Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 200 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 250 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179 | 3.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 4.0 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180 | 3.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180 | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | ISO2039-1 | 160 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.