PA6 Ultramid® B3EG10 BASF GERMANY
129
- Unit Price:
- $3866 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Oil resistant
- Application Areas:Thin walled components Plastic accessories Shell
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 4.5 到 5.1 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 1.3 到 1.7 | % | |
| Apparent Density | 0.70 | g/cm³ | ||
| Melt Volume flow Rate | 275°C/5.0 kg | ISO 1133 | 15.0 | cm3/10min |
| Viscosity number | 96% H2SO4 | ISO 307 | 135 | cm³/g |
| Modeling Shrinkage | 0.30 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO 178 | 320 | Mpa | |
| Tensile Creep Modulus | 1000 hr | ISO 899-1 | 7400 | Mpa |
| Tensile Stress | Break | ISO 527-2 | 235 | Mpa |
| Tensile Strain | Break | ISO 527-2 | 3.0 | % |
| Tensile Modulus | ISO 527-2 | 16000 | Mpa | |
| Flexural Modulus | ISO 178 | 15000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 220 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 215 | °C | |
| Linear thermal expansion coefficient | Flow : 23 to 80°C | ISO 11359-2 | 1.0E-5 到 1.5E-5 | cm/cm/°C |
| Across Flow : 23 to 80°C | ISO 11359-2 | 5.0E-5 到 6.0E-5 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 220 | °C | |
| Specific Heat | 1300 | J/kg/°C | ||
| Thermal Conductivity | DIN 52612 | 0.38 | W/m/K | |
| Maximum Service Temperature (short cycle operation) | 200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 1 MHz | IEC 60250 | 4.20 | |
| Comparative Tracking Index | Solution A | IEC 60112 | 550 | V |
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.014 | |
| Surface Resistivity | IEC 60093 | 1.0E+10 | ohms | |
| Volume Resistivity | IEC 60093 | 1.0E+15 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Residence Time | < 10.0 | min | ||
| Screw Speed | < 18 | m/min | ||
| Drying Temperature | 80 | °C | ||
| Suggested Max Moisture | 0.15 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Mold Temperature | 80 到 90 | °C | ||
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 270 | °C | ||
| Middle Temperature | 280 | °C | ||
| Front Temperature | 290 | °C | ||
| Nozzle Temperature | 290 | °C | ||
| Hopper Temperature | 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 90 | kJ/m² |
| 23°C | ISO 179/1eU | 100 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Halogen Content | 内部方法 | < 100 | mg/kg | |
| Polymer Abbreviation | PA6-GF50 | |||
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.