Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23℃ | ISO 62 | 10 | % |
Moisture Absorption | 23℃50RHEquilibrium | ISO 62 | 3 | % |
Modeling Shrinkage | Flow150x105x3mm 270℃ 50MPa模具温 度:80℃ | ISO 2577 | 1.02 | % |
Modeling Shrinkage | 垂直150x105x3mm 270°C 50Mpa模具温 度:80℃ | ISO 2577 | 1.16 | % |
Modeling Shrinkage | Flow 150xW5x3mm120°C4hr | ISO 2577 | 0.32 | % |
Modeling Shrinkage | 垂直 150x105x3mm 120°C4hr | ISO 2577 | 0.4 | % |
proportion | | ISO 1183 | 1140 | kg/㎥ |
Apparent (Bulk) Density | | ISO 60 | 700 | kg/㎥ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Film Puncture Force | 最大力23℃ | ISO 6603 | 5900 | N |
Film Puncture Force | 最大力-30℃ | ISO 6603 | 7300 | N |
Film Puncture Force | 23℃ | ISO 6603 | 90 | J |
Film Puncture Force | -30℃ | ISO 6603 | 85 | J |
Notched Izod Impact Strength | 23℃ | ISO 180 | (10干态)(30湿态) | kJ/m² |
Charpy Unnotched Impact Strength | 23℃ | ISO 179 | (NB干态)(NB湿态) | kJ/m² |
Charpy Unnotched Impact Strength | -30℃ | ISO 179 | (NB干态)(NB湿态) | kJ/m² |
Unnotched Izod Impact Strength | 23℃ | ISO 180 | (NB干态)(NB湿态) | kJ/m² |
Unnotched Izod Impact Strength | -30℃ | ISO 180 | (NB干态)(NB湿态) | kJ/m² |
Tensile Creep Modulus | 1hr | ISO 899 | (800湿态) | Mpa |
Tensile Creep Modulus | 1000hr | ISO 899 | (600湿态) | Mpa |
Charpy Notched Impact Strength | 23℃ | ISO 179 | (10干态)(20湿态) | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO 179 | (10干态)(10湿态) | kJ/m² |
Flexural Strain | 2.0mm/min | ISO 178 | (6干态)(8湿态) | % |
Tensile Modulus | 1.0mm/min | ISO 527 | (3200干态)(1000湿态) | Mpa |
Tensile Strength | Yield50mm/min | ISO 527 | (80干态)(40湿态) | Mpa |
Tensile Elongation | Yield50mm/min | ISO 527 | (4干态)(20湿态) | % |
Tensile Elongation | Break50mm/min | ISO 527 | (20干态)(50湿态) | % |
Flexural Modulus | 2.0mm/min | ISO 178 | (2900干态)(850湿态) | Mpa |
Flexural Strength | 2.0mm/min | ISO 178 | (110干态)(35湿态) | Mpa |
Flexural Strength | 3.5%Strain 2.0mm/min | ISO 178 | (95干态)(25湿态) | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa | ISO 75 | 55 | °C |
Deflection Temperature Under Load? | 0.45MPa | ISO 75 | 160 | °C |
Deflection Temperature Under Load? | 8.0MPa | ISO 75 | 45 | °C |
Melting temperature | 10℃/min | ISO 11357 | 222 | °C |
Coefficient of Linear Thermal Expansion | Flow23~550℃ | ISO 11359 | 0.00010 | cm/cm/℃ |
Coefficient of Linear Thermal Expansion | 垂直23~55℃ | ISO 11359 | 0.00011 | cm/cm/℃ |
Vicat Softening Temperature | 120℃/hr 50N | ISO 306 | 200 | °C |
Vicat Softening Temperature | 50℃/hr 50N | ISO 306 | 200 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Insulation strength | 1.0mm | IEC 60243 | (30干态)(30湿态) | KV/mm |
Volume Resistivity | | IEC 60093 | (10000000000000干态)(10000000000湿态) | Ω.m |
Surface resistance | | IEC 60093 | (100000000000000干态)(10000000000000湿态) | Ω |
CTI | 溶液A | IEC 60112 | 600 | V |
CTI | M溶液B | IEC 60112 | 600 | V |
Dielectric Constant | 100Hz | IEC 60250 | (4干态)(15湿态) | |
Dielectric Constant | 1MHz | IEC 60250 | (3.5干态)(4湿态) | |
Dissipation Factor | 100Hz | IEC 60250 | (0.017干态)(0.2湿态) | |
Dissipation Factor | 1MHz | IEC 60250 | (0.02干态)(0.12湿态) | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO 2039 | (140干态)(50湿态) | n/mm² |
Flame Rating | Test Condition | Test Method | Test Result | Unit |
---|
Fire rating | 本色638mm | UL94 | V-2 | |
Fire rating | 全色1.5mm | UL94 | \A2 | |
Fire rating | 全色3.0mm | UL94 | U2 | |
Fire rating | 全色6.0mm | UL94 | V-2 | |
Glow Wire Ignition Temperature | 2.0mm | IEC 60695 | 750 | °C |
Oxygen Index | 方法A | ISO 4589 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.