Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 230°C/2.16kg | ISO 527-2/5, ISO 527-2/50 | 0.01到0.07 | |
23℃ | | g/cm³ | 0.969到1.25 | |
23℃ | | % | 0.87到1.2 | |
23℃,24hr | | % | 0.020到0.052 | |
23℃,24hr | | % | 0.030到0.050 | |
Flow:23℃ | | mm/mm | 0.279到0.457 | |
Flow:23℃ | | mm/mm | 139.7E-3到0.432 | |
230°C/2.16kg | | g/10min | 0.95到20 | |
230°C/2.16kg | | g/10min | 4.9到21 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
23℃ | | MPa | 1979.31到4220.69 | |
23℃ | | MPa | 1841.38到4220.69 | |
23℃ | | MPa | 44.76到50.62 | |
23℃ | | MPa | 33.79到62.48 | |
23℃ | | MPa | 1875.86到4324.14 | |
23℃ | | MPa | 30.0到35.52 | |
23℃ | | MPa | 1400.0到4703.45 | |
Break,23℃ | | % | 2.0到31 | |
Break,23℃ | | MPa | 44.76到59.03 | |
Break,23℃ | | MPa | 21.72到30.28 | |
Break,23℃ | | % | 3.7到31 | |
Break,23℃ | | MPa | 19.03到32.83 | |
Yield,23℃ | | % | 2.6到7.2 | |
Yield,23℃ | | % | 1.7到8.4 | |
Yield,23℃ | | MPa | 27.93到35.24 | |
Yield,23℃ | | MPa | 28.41到36.76 | |
Yield,23℃ | | MPa | 51.38到55.59 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
0.45MPa, Unannealed | | °C | 109到133 | |
0.45MPa, Unannealed | | °C | 110到139 | |
1.8MPa, Unannealed | | °C | 58到91 | |
1.8MPa, Unannealed | | °C | 59到91 | |
-- | | °C | 165到182 | |
-- | | mm/mm/°C | 83.8E-5到101.6E-5 | |
-- | | °C | 88到157 | |
-- | | °C | 85到156 | |
-- | | °C | 160 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ohms | 1.0E+14到1.0E+15 | |
Comparative Tracking Index | | V | 596到600 | |
23℃ | | ohms·cm | 9.8E+15到1.0E+16 | |
23℃ | | ohms·cm | 1.0E+13到1.0E+15 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 2.229到8.821 | |
Gardner Impact | 23℃ | N.m | 26.55到73.89 | |
Gardner Impact | 23℃ | N.m | 8.85到80.35 | |
23℃ | | kJ/m² | 1.858到2.089 | |
23℃ | | J/m | 0.070到0.203 | |
23℃ | | kJ/m² | 0.442到1.347 | |
23℃ | | J/m | 0.007到0.013 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
23℃ | | | 63到78 | |
23℃ | | | 72到79 | |
Rockwell Hardness | 23℃ | | 84到106 | |
Ball Indentation Hardness | | MPa | 74.48到85.52 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Gardner | | | 46到47 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | | °C | 643到960 | |
Oxygen Index | | % | 21 | |
Glow Wire Ignition Temperature | | °C | 548到804 | |
Burning Rate | | mm/min | 0.0到101.6 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.