Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.40到0.70 | % |
Moisture Absorption | Saturation,23°C | ISO62 | <0.10 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | <0.10 | % |
Melt Volume flow Rate | 200°C/5.0kg | ISO1133 | 5.50 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 44.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 30.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 1.6 | % |
Tensile Strain | Break,23°C | ISO527-2 | 30 | % |
Tensile Modulus | | ISO527-2 | 2050 | Mpa |
Flexural Modulus | | ISO178 | 2100 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | -- | ISO306/A50 | 98.0 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 90.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 88.0 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 78.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1.50mm | IEC60243-1 | 160 | KV/mm |
Dissipation Factor? | 1MHz | IEC60250 | 4E-04 | |
Surface Resistivity | | IEC60093 | >1.0E+13 | ohms |
Dielectric Constant | 100Hz | IEC60250 | 2.50 | |
Dielectric Constant | 1MHz | IEC60250 | 2.50 | |
Volume Resistivity | | IEC60093 | >1.0E+18 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 70 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 120 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 83.0 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Gardner | 60° | ASTMD523 | 70 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.