GPPS GPPS-123P SECCO SHANGHAI
294
- Unit Price:
- $1210 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 81MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molding shrinkage rate | ASTM D955 | 0.4-0.6 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | <0.1 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 8.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | ASTM D790/ISO 178 | 3100 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 75 | kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 50 | % | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 9 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 73 | ℃（℉） | |
| vicat softening point | ASTM D1525/ISO R306 | 91 | ℃（℉） |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold temperature | 30-60 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.