GPPS POLYREX® PG-33 ZHENJIANG CHIMEI
298
- Unit Price:
- $1417 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 138.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant transparent
- Application Areas:Lampshade Household goods Audiotape container Food containers Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ISO294-4 | 0.40to0.70 | % | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 8.0 | g/10min |
| Melt volume flow rate | 200°C/5.0kg | ISO1133 | 8.00 | cm3/10min |
| Density/specific gravity 2 | ASTMD792 | 1.05 | g/cm³ | |
| Density/specific gravity | 23°C | ISO1183 | 1.04 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength 3 | Break | ASTMD638 | 45.0 | Mpa |
| Bending modulus 4 | ASTMD790 | 3030 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 2.0 | % |
| Bending modulus 5 | ISO178 | 3100 | Mpa | |
| Bending strength 6 | ASTMD790 | 65.6 | Mpa | |
| Bending stress 5 | ISO178 | 75.0 | Mpa | |
| Tensile stress | Break | ISO527-2/50 | 48.0 | Mpa |
| Tensile strain | Break | ISO527-2/50 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 5.0E-5to8.0E-5 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 79.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 76.0 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 87.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 87.0 | °C | |
| Vicat softening temperature | ASTMD15257 | 94.0 | °C | |
| -- | ISO306/A50 | 94.0 | °C | |
| -- | ISO306/B50 | 90.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 1.8 | kJ/m² |
| 23°C | ISO179 | 2.7 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 17 | J/m |
| 23°C,6.40mm | ASTMD256 | 15 | J/m | |
| -30°C | ISO180/1A | 1.8 | kJ/m² | |
| 23°C | ISO180/1A | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTMD785 | 77 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.