ABS ECO GP-22 MR50 INEOS STYRO KOREA
124
- Unit Price:
- $2055 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Impact resistance Heat resistant deformatio
- Application Areas:Electrical enclosure electronic product Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD | ASTMD955 | 0.40to0.70 | % |
| ISO294-4 | 0.40to0.70 | % | ||
| Moisture Absorption | Saturation,23°C | ASTMD570 | 1.0 | % |
| Saturation,23°C | ISO62 | 1.0 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.22 | % | |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 1.5 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 19 | g/10min | |
| Melt Volume flow Rate | 230°C/3.8kg | ASTMD1238 | 4.80 | cm3/10min |
| 220°C/10.0kg | ISO1133 | 19.0 | cm3/10min | |
| Density / Specific Gravity | ASTMD792 | 1.04 | g/cm³ | |
| ISO1183 | 1.04 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 10 | % |
| Flexural Stress | ISO178 | 65.0 | Mpa | |
| Tensile Strength | Yield,23°C | ASTMD638 | 45.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 45.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 2.6 | % |
| Tensile Modulus | ASTMD638 | 2300 | Mpa | |
| ISO527-2 | 2300 | Mpa | ||
| Tensile Elongation | Break | ASTMD638 | 2.6 | % |
| Flexural Modulus | ASTMD790 | 2300 | Mpa | |
| Flexural Strength | ASTMD790 | 65.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 90.6 | °C |
| 0.45MPa,Annealed | ASTMD648 | 104 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 77.8 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 98.9 | °C | |
| Vicat Softening Temperature | -- | ISO306/A50 | 105 | °C |
| -- | ISO306/B50 | 96.0 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 8.0E-5to1.1E-4 | cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 99.0 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 94.0 | °C | |
| Thermal Conductivity | DIN52612 | 0.17 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 4.8E-03 | |
| 1MHz | IEC60250 | 7.9E-03 | ||
| Relative Permittivity | 100Hz | IEC60250 | 2.90 | |
| 1MHz | IEC60250 | 2.80 | ||
| Surface Resistivity | IEC60093 | 1E+13 | ohms | |
| Dielectric Constant | 1.00mm,1MHz | ASTMD150 | 2.80 | |
| Volume Resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 100 | kJ/m² |
| 23°C | ISO179 | 180 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 8.0 | kJ/m² |
| 23°C | ISO179 | 22 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 59 | J/m |
| -18°C | ASTMD256 | 100 | J/m | |
| 23°C | ASTMD256 | 300 | J/m | |
| -30°C | ISO180/A | 8.0 | kJ/m² | |
| 23°C | ISO180/A | 26 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 103 | |
| Ball Indentation Hardness | ISO2039-1 | 97.0 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| The Yellow Index | DIN6167 | 13 | YI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.