Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 220℃/10.0Kg | ISO1133 | 31 | g/10min |
Melt Mass-Flow Rate | 线性收缩率 | ISO294-4 | 0.4-0.7 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 110 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 90 | kJ/m² |
Tensile Elongation?(Break) | Yield,23°C | ISO527-2 | 2.6 | % |
Tensile Elongation?(Break) | 23°C | ISO527-2 | >=15 | % |
Tensile Modulus | 23°C | ISO527-2 | 2400 | Mpa |
Tensile Strength | Yield,23°C | ISO527-2 | 46 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
Flexural Strength | 23°C | ISO178 | 70 | Mpa |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 15 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 15 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/1A | 7 | kJ/m² |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | 5.10kg | ISO306/A50 | 99 | °C |
Deflection Temperature Under Load? | 0.45MPaUnannealed | ISO75-2/Bf | 98 | °C |
Deflection Temperature Under Load? | 1.80MPaAnnealed | ISO75-2/Af | 94 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | | IEC60250 | 2.9 | 1MHz |
Dielectric Constant | | IEC60250 | 3 | 100HZ |
Dissipation Factor? | | IEC60250 | 0.05 | |
Dissipation Factor? | | IEC60250 | 0.09 | |
Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 600 | V |
Insulation strength | 1.00mm | IEC60243-1 | 35 | KV/mm |
Volume Resistivity | | IEC60093 | 1E+13 | Ω.cm |
Surface resistance | | IEC60093 | 1E+15 | Ω.cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 110 | Mpa |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Melting temperature | | ISO294 | 240 | °C |
Injection Rate | | ISO294 | 240 | mm/sec |
Burning rate | | ISO3795 | 60 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.