ABS Novodur® HH-112 BK10009 INEOS STYRO KOREA
222
- Unit Price:
- $2801 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 55MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting High rigidity
- Application Areas:Automotive sector Application in the automo Automotive interior parts Automotive External Parts
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.25 | % |
| ASTM D570 | 0.3 | % | ||
| Shrinkage rate | MD | ASTMD955 | 0.55 | % |
| ISO294-4 | 0.40to0.70 | % | ||
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 6.0 | g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Yield elongation rate | ISO 527-2 | 3.0 | % | |
| Ball pressure hardness | ISO2039-1 | 114 | Mpa | |
| Tensile strength at break | ISO 527-2 | 390 | kg/cm | |
| Yield tensile strength | ISO 527-2 | 580 | kg/cm | |
| Nominal tensile fracture strain | 23°C | ISO527-2 | 8.0 | % |
| Bending stress | ISO178 | 81.0 | Mpa | |
| Tensile stress | Yield,23°C | ISO527-2 | 58.0 | Mpa |
| Tensile strain | Yield,23°C | ISO527-2 | 3.1 | % |
| Tensile strength | Yield,23°C | ASTMD638 | 58.0 | Mpa |
| Tensile modulus | ASTMD638 | 2800 | Mpa | |
| ISO527-2 | 2700 | Mpa | ||
| ISO 527-2 | 28000 | kg/cm | ||
| elongation | Break | ISO 527-2 | 20 | % |
| Break | ASTMD638 | 3.0 | % | |
| Rockwell hardness | 115 | R | ||
| Bending modulus | ISO 178 | 27000 | kg/cm | |
| ASTMD790 | 2700 | Mpa | ||
| ISO178 | 2700 | Mpa | ||
| bending strength | ASTMD790 | 88.3 | Mpa | |
| ISO 178 | 880 | kg/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8Mpa | ASTM D648 | 109 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 118 | °C |
| -- | ISO306/B50 | 112 | °C | |
| ISO 306 | 112 | °C | ||
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Flame retardancy | UL94 | HB | ||
| Hot deformation temperature 2 | 0.45MPa,Annealed | ISO75-2/B | 110 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 102 | °C | |
| Maximum operating temperature | 90 | °C | ||
| thermal conductivity | DIN52612 | 0.17 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrical strength | 1.50mm | IEC60243-1 | 41 | KV/mm |
| Leakage Trace Index | IEC60112 | 600 | V | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| IEC60093 | 1E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 80 | kJ/m² |
| 23°C | ISO179 | 140 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.