ABS Novodur® HH-106 BK10009 INEOS STYRO THAILAND
131
- Unit Price:
- $2800 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting
- Application Areas:Electronic field Automotive sector Application in the automo Automotive interior parts
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | ASTM D570 | 0.3 | % | |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Modeling Shrinkage | MD | ASTMD955 | 0.55 | % |
| ISO294-4 | 0.40to0.70 | % | ||
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.25 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2500 | Mpa | |
| ISO527-2 | 2400 | Mpa | ||
| Tensile Strength | Yield,23°C | ASTMD638 | 52.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 51.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 3.0 | % |
| Tensile Elongation | Break | ASTMD638 | 3.0 | % |
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 9.0 | % |
| Flexural Modulus | ASTMD790 | 2400 | Mpa | |
| ISO178 | 2400 | Mpa | ||
| Flexural Strength | ASTMD790 | 77.2 | Mpa | |
| Flexural Stress | ISO178 | 72.0 | Mpa | |
| Tensile Strength(Yield) | ISO 527-2 | 520 | kg/cm | |
| Tensile Strength(Break) | ISO 527-2 | 390 | kg/cm | |
| Tensile Elongation (Break) | ISO 527-2 | 3.0 | % | |
| Tensile Elongation | Break | ISO 527-2 | 25 | % |
| Tensile Modulus | ISO 527-2 | 25000 | kg/cm | |
| Flexural Strength | ISO 178 | 770 | kg/cm | |
| Flexural Modulus | ISO 178 | 24000 | kg/cm | |
| Rockwell Hardness | 110 | R | ||
| Vicat Softening Temperature | ISO 306 | 103 | °C | |
| Ball Indentation Hardness | ISO2039-1 | 102 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 107 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 99.0 | °C | |
| Vicat Softening Temperature | -- | ISO306/A50 | 115 | °C |
| -- | ISO306/B50 | 106 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Thermal Conductivity | DIN52612 | 0.17 | W/m/K | |
| Maximum Service Temperature | 85 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| IEC60093 | 1E+15 | ohms·cm | ||
| Electric strength | 1.50mm | IEC60243-1 | 39 | KV/mm |
| Comparative Tracking Index | IEC60112 | 600 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 100 | kJ/m² |
| 23°C | ISO179 | 190 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.