Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | 内部方法 | 0.40to0.60 | % |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 25 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | | ASTMD638 | 48.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 54.0 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 17 | % |
| Flexural Stress | 23°C | ISO178 | 77.0 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 20 | % |
| Flexural Modulus | | ASTMD790 | 2160 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2260 | Mpa |
| Flexural Strength | | ASTMD790 | 74.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 83.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 77.0 | °C |
| Vicat Softening Temperature | | | 90.0 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | ASTMD785 | 115 | |
| Rockwell Hardness | R-Sale,23°C | ISO2039-2 | 115 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | Total,3000μm | ISO13468 | 88.0 | % |
| Haze | 3000µm | ISO14782 | 2.0 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.